Biodegradable adhesive tape and biodegradable adhesive label

ABSTRACT

An adhesive tape or an adhesive label each of which comprises a substrate including a biodegradable polymer layer and an adhesive layer provided on at least one surface of the substrate. The adhesive tape has a release agent layer formed on an opposite surface to the surface where the adhesive layer is provided, or has a release tape which is in contact with the adhesive layer, and the adhesive tape was wound up around a core for storage. The adhesive label has a release sheet which is in contact with the adhesive layer. In such biodegradable adhesive tape and biodegradable adhesive label, a biodegradable polymer is used as a material of the substrate, and therefore the tape and label do not disrupt the natural environment or do not largely disorganize the ecosystem in the soil even when discarded in the soil after use.

FIELD OF THE INVENTION

The present invention relates to an adhesive tape and an adhesive labeleach of which comprises a substrate in the form of a tape, a film oretc. and an adhesive layer provided on said substrate. Moreparticularly, the invention relates to a biodegradable adhesive tape anda biodegradable adhesive label each of which can be degraded by microbeswhen discarded in the soil so as not to exert bad influence on thenatural environment.

BACKGROUND OF THE INVENTION

Adhesive tapes and adhesive labels each of which comprises a substratein the form of a tape, a film or etc. and an adhesive layer formed onthe substrate are conventionally known.

Examples of the adhesive tapes include a single-sided adhesive tapecomprising a release agent layer formed on one surface of an adhesivetape substrate and an adhesive layer formed on the other surface of thesubstrate; and a double-sided adhesive tape comprising a double-sidedadhesive tape main body which has an adhesive tape substrate bearingadhesive layers on both surfaces thereof and a double-sided release tapehaving a release tape substrate bearing release agent layers on bothsurfaces thereof, which adheres to one of the surfaces of the adhesivetape main body.

The adhesive tapes are stored or on the market as rolls formed bywinding those tapes around a paper core or a plastic core. In the caseof the single-sided adhesive tape, the adhesive tape itself is rolled upvia its release agent layer so that the adhesive layers are not directlybrought into contact with each other. In the case of the double-sidedtape, the double-sided adhesive tape main body is rolled up via therelease tape so that the adhesive layers are not directly brought intocontact with each other.

Examples of the adhesive labels include an adhesive label whichcomprises an adhesive label main body having an adhesive label substrateand an adhesive layer laminated thereon and a release sheet having apaper sheet and a release agent layer provided thereon, in which theadhesive layer of the adhesive label main body is adhered to the releaseagent layer of the release sheet.

For the use of the adhesive label of this type, the adhesive label mainbody is released from the release sheet.

As the substrates of the adhesive tapes and the adhesive labels referredto the above, plastic substrates have been mainly used conventionally.For the disposal of the conventional adhesive tapes and adhesive labelsafter use, they are incinerated or buried in the soil.

However, such disposal involves the following problems.

(1) Problems in disposal by incinerating.

When the adhesive tapes and adhesive labels including the plasticsubstrate are incinerated, energy of high intensity is required forburning the plastic substrate. Further, carbon dioxide is generated byburning of the plastic substrate, and thereby warming of the earth maybe accelerated. Particularly when the plastic substrate is polyvinylchloride, a hydrogen chloride gas is generated to cause acid rain.

(2) Problems in the disposal by burying in the soil.

Recently, waste disposal by burying the waste in the soil has beenmarkedly increased, and hence it is difficult to keep a site for thewaste disposal. Further, if the adhesive tapes and the adhesive labelsare buried in the soil, the plastic materials used for their substratesstably exist for a long period of time, and thereby the naturalenvironment is disrupted or the ecosystem in the soil is disorganized.

It can be thought to separate the plastic substrates from the adhesivetapes and the adhesive labels after use to recycle them. However, theseparation and the collection of the plastic substrates require anenormous cost, and this results in bad marketability. In addition, suchrecycled plastic substrates are deteriorated in quality.

OBJECT OF THE INVENTION

The present invention is intended to solve such problems associated withthe prior art technique as described above, and it is an object of theinvention to provide an adhesive tape and an adhesive label each ofwhich does not disrupt the natural environment or does not disorganizethe ecosystem in the soil even when discarded in the soil after use.

SUMMARY OF THE INVENTION

The first biodegradable adhesive tape according to the inventioncomprises an adhesive tape substrate including a biodegradable polymerlayer, a release agent layer formed on one surface of said substrate andan adhesive layer formed on the other surface of said substrate.

The second biodegradable adhesive tape according to the inventioncomprises a biodegradable double-sided adhesive tape main bodycomprising an adhesive tape substrate including a biodegradable polymerlayer and adhesive layers formed on both surfaces of the adhesive tapesubstrate; and a double-sided release tape comprising a release tapesubstrate and release agent layers formed on both surfaces of therelease tape substrate, wherein the biodegradable double-sided adhesivetape main body and the double-sided release tape are laminated togetherin such a manner that the adhesive layer of the biodegradabledouble-sided adhesive tape main body is in contact with the releaseagent layer of the double-sided release tape.

The biodegradable adhesive label according to the invention comprises abiodegradable adhesive label main body comprising an adhesive labelsubstrate including a biodegradable polymer layer and an adhesive layerlaminated on the adhesive label substrate, and a release sheetcomprising a release sheet substrate including a layer formed from amaterial selected from a paper, a non-biodegradable polymer and abiodegradable polymer and a release agent layer formed on the releasesheet substrate, wherein the biodegradable adhesive label main body andthe release sheet are laminated together in such a manner that theadhesive layer of the biodegradable adhesive label main body is incontact with the release agent layer of the release sheet.

In the first adhesive tape, the second adhesive tape and the adhesivelabel according to the invention, each of the adhesive tape substrateand the adhesive label substrate may be made up of only thebiodegradable polymer layer. Further, each of these substrates may be alaminate composed of the biodegradable polymer layer and a paper layer.Otherwise, it may be a laminate having the laminated structure:biodegradable polymer layer/paper layer/biodegradable polymer layer.Moreover, the adhesive tape substrate may be a laminate of abiodegradable polymer layer and any one of a metallic thin film and ametallic oxide thin film.

The release tape substrate used in the second adhesive tape of theinvention may be made up of only a biodegradable polymer layer or only apaper layer. Otherwise, it may be a laminate having the laminatedstructure: biodegradable polymer layer/paper layer/biodegradable polymerlayer.

In the adhesive label of the invention, the release sheet substrate maybe made up of only a paper layer, only a non-biodegradable polymer layeror only a biodegradable polymer layer. This release sheet substrate maybe a laminate of a paper layer and any one of a non-biodegradablepolymer layer and a biodegradable polymer layer. Otherwise, it may be alaminate having the laminated structure: non-biodegradable polymerlayer/paper layer/non-biodegradable polymer layer, or the laminatedstructure: biodegradable polymer layer/paper layer/biodegradable polymerlayer.

BRIEF DESCRIPTION OF THE DRAWING

FIG. 1 is a schematic sectional view showing one preferred embodiment ofthe first biodegradable adhesive tape according to the presentinvention.

FIGS. 2 to 4 are each a schematic sectional view showing anotherpreferred embodiment of the first biodegradable adhesive tape accordingto the present invention,

FIG. 5 is a schematic sectional view showing one preferred embodiment ofthe second biodegradable adhesive tape according to the presentinvention.

FIGS. 6 to 16 are each a schematic sectional view showing anotherpreferred embodiment of the second biodegradable adhesive tape accordingto the present invention.

FIG. 17 is a schematic sectional view showing the biodegradable adhesivelabel according to the present invention.

FIGS. 18 to 29 are each a schematic sectional view showing anotherpreferred embodiment of the biodegradable adhesive label according tothe present invention.

DETAILED DESCRIPTION OF THE INVENTION

The biodegradable adhesive tape and the biodegradable adhesive labelaccording to the invention will be described below in more detail withreference to their preferred embodiments.

The first biodegradable adhesive tape of the invention is now describedwith reference to FIGS. 1 to 4 of the attached drawings. FIGS. 1 to 4are each an enlarged sectional view showing one preferred embodiment ofthe first biodegradable adhesive tape according to the invention.

In the biodegradable adhesive tape 10 shown in FIG. 1, a release agentlayer 3 is formed on one surface of an adhesive tape substrate 1 whichis made up of only a biodegradable polymer layer (a), and an adhesivelayer 2 is formed on the other surface of the adhesive tape substrate 1.

As a material of the biodegradable polymer layer (a), any biodegradablepolymers may be used as far as they can be degraded by organism(microbes) existing in the natural world to be finally turned into suchas carbon dioxide and water, that is, they have so-calledbiodegradability. Listed below are preferred examples of thebiodegradable polymers used for forming the biodegradable polymer layer.

a) linear polyester of 3-hydroxybutyric acid and 3-hydroxyvaleric acid(trade name: Biopole, available from ICI Co., England);

This linear polyester (Biopole) is obtained by sugar fermentation byAlcaligenes Europhus.

b) lactic acid type biodegradable polymers prepared by ring-openingpolymerization of lactide which is obtained by lactic acid fermentationof glucose (available from Shimazu Seisakusho Co.);

c) biodegradable polymers prepared from natural polymers such as starch,polysaccharides and chitin (e.g., Pulran (trade name) available fromRinbara Kenkyusho);

d) biodegradable polycaprolactone obtained by ring-openingpolymerization of ε-caprolactam;

e) biodegradable polymers such as polyvinyl alcohol and denaturedproducts thereof (trade name: Biotex, available from Air Product andChemicals Co., U.S.A.);

f) biodegradable polymers such as polyether, polyacrylic acid,ethylene/carbon monoxide copolymer, aliphatic polyester/polyamidecopolymer, aliphatic polyester/polyolefin copolymer, aliphaticpolyester/aromatic polyester copolymer and aliphatic polyester/polyethercopolymer;

g) biodegradable polymers such as polylactic acid, polybutyric acid,polyglycolide and derivatives thereof;

h) polymer alloy of starch and denatured polyvinyl alcohol (trade name:Matabee, available from Novamont Co., U.S.A.);

i) polymer alloy of starch and polyethylene (trade name: Polygrade II,available from Anpacette Co.; trade name: Polyclean, available fromArker Daniel Midland Co., U.S.A.);

j) composition of silane starch and polyethylene (trade name: Ecostar,available from St. Laurence Starch Co.); and

k) polymer alloy of polycaprolactone and polyethylene (trade name:Biomicron, available from JSP Co.; trade name: Tone, available fromUnion Carbide Co., U.S.A.).

When the biodegradable adhesive tape 10 having a biodegradable polymerlayer formed from the above-mentioned polymers is discarded in the soil,the biodegradable polymer layer (a) is degraded by microbes in the soilinto such as carbon dioxide and water.

The thickness of the adhesive tape substrate 1 made up of only thebiodegradable polymer layer (a) is in the range of usually 12 to 125 μm,preferably 25 to 100 μm.

Such adhesive tape substrate 1 can be prepared by subjecting theabove-mentioned biodegradable polymer, e.g., a mixture of starch anddenatured polyvinyl alcohol, to a film-forming process such as inflationor T-die casting. The resulting film is then subjected to stretching asa post treatment if necessary, so as to have a desired thickness.

Examples of the release agent for forming the release agent layer 3include release agents of natural compounds such as shellac, naturalwax, casein and starch, and synthetic release agents such as polyvinylalcohol, derivatives thereof and silicone. They can be used singly or incombination.

Some of the release agents of natural compounds and some of thesynthetic release agents such as polyvinyl alcohol and derivativethereof exhibit biodegradability.

In the present invention, the release agent layer 3 is preferably formedfrom the biodegradable release agents, because the natural environmentis not disrupted even when the biodegradable adhesive tape 10 isdiscarded in the soil.

The thickness of the release agent layer 3 is in the range of usually0.01 to 1 μm, preferably 0.03 to 0.1 μm.

The release agent layer 3 can be formed by coating the upper surface ofthe adhesive tape substrate 1 with the release agent as mentioned aboveby means of, for example, a roll coater.

The adhesive for forming the adhesive layer 2 in the biodegradableadhesive tape 10 is, for example, an adhesive made of a mixture of anatural rubber and at least one tackifier resin selected from the groupconsisting of rosin, derivatives of rosin (e.g., hydrogenated rosin,disproportionated rosin, polymerized rosin and rosin ester), terpene,and derivatives of terpene (e.g., α-pinene resin, β-pinene resin,dipentene resin and hydrogenation products of these resins). The naturalrubber may be in the form of either a solid or a latex. In the adhesive,the tackifier resin is preferably used in an amount of 1 to 150 parts byweight based on 100 parts by weight of the natural rubber.

Since the above-mentioned adhesive exhibits biodegradability, it can befavorably used for forming the adhesive layer 2 in the invention.

The biodegradable adhesive tape 10 consisting of the adhesive tapesubstrate 1 exhibiting biodegradability, the release agent layer 3exhibiting biodegradability and the adhesive layer 2 exhibitingbiodegradability especially does not disrupt the natural environmenteven when it is discarded in the soil.

An acrylic type adhesive conventionally widely used is also employableas the adhesive. The acrylic type adhesive is ordinarily deterioratedand decomposed when it is discarded in the soil.

The amount of the adhesive for forming the adhesive layer 2 is in therange of usually 10 to 100 g/m², preferably 20 to 50 g/m².

The adhesive layer 2 can be obtained by, for example, coating the lowersurface of the adhesive tape substrate 1 with a solution of theabove-mentioned adhesive and drying the solution at a temperature of 50°to 120° C.

Examples of solvents used for preparing the coating solution of theadhesive include toluene, xylene and ethyl acetate.

The biodegradable adhesive tape 10 shown in FIG. 2 is the same as thebiodegradable adhesive tape 10 shown in FIG. 1 except for the adhesivetape substrate 1.

In the biodegradable adhesive tape 10 shown in FIG. 2, the adhesive tapesubstrate 1 is composed of a laminate of a biodegradable polymer layer(a) and a paper layer (b), and the paper layer (b) is provided betweenthe biodegradable polymer layer (a) and the adhesive layer 2.

The polymer of the biodegradable polymer layer (a) and the thickness ofthe polymer layer are the same as those described above.

The thickness of the paper layer (b) is determined in such a manner thatthe weight of the paper layer (b) is in the range of usually 50 to 150g/m², preferably 60 to 100 g/m².

The adhesive tape substrate 1 composed of the laminate of thebiodegradable polymer layer (a) and the paper layer (b) can be obtainedby, for example, laminating the biodegradable polymer layer (a) on thepaper layer (b) at a temperature of 100° to 300° C. using an extrusionmolding machine.

The biodegradable adhesive tape 10 shown in FIG. 3 is the same as theadhesive tape 10 shown in FIG. 1 except for the adhesive tapesubstrate 1. In the biodegradable adhesive tape 10 shown in FIG. 3, theadhesive tape substrate 1 is composed of a laminate having the laminatedstructure: biodegradable polymer layer (a)/paper layer (b)/biodegradablepolymer layer (a).

The adhesive tape substrate 1 having such a three-layered structure asmentioned above can be obtained in the same manner as for the adhesivetape substrate 1 shown in FIG. 2. except that the biodegradable polymerlayer (a), the paper layer (b) and the biodegradable polymer layer (a)are superposed one upon another in this order.

In the biodegradable adhesive tape 10 shown in FIG. 4, the adhesive tapesubstrate 1 is composed of a laminate of a biodegradable polymer layer(a) and a metallic thin film (c), and the metallic thin film (c) isprovided between the biodegradable polymer layer (a) and the adhesivelayer 2. In place of the metallic thin film (c), a metallic oxide thinfilm such as a silica thin film may be provided.

The biodegradable polymer layer (a) and the thickness thereof are thesame as those described above.

As the metallic thin film (c), a thin film of aluminum, brass, chromiumor the like can be used. The thickness of the metallic thin film (c) isin the range of usually 50 to 1,000 angstrom, preferably 100 to 300angstrom.

The adhesive tape substrate 1 composed of the laminate of thebiodegradable polymer layer (a) and the metallic thin film (c) can beobtained by, for example, forming the metallic thin film (c) such as analuminum thin film on the biodegradable polymer layer a by means ofvacuum deposition, sputtering, ion plating, etc. When the metallic thinfilm (c) is formed on the biodegradable polymer layer (a) by vacuumdeposition, the degree of vacuum is adjusted to be in the range of1×10⁻⁴ to 1×10⁻⁵ torr. The metallic thin film thus formed on thebiodegradable polymer layer (a) generally has an oxygen permeabilityconstant of 1×10⁻¹² to 1×10⁻¹⁴ cm³ (STP).cm/cm².sec.cmHg.

Each of the biodegradable adhesive tapes 10 shown in FIGS. 1 to 4 is asingle-sided adhesive tape, and it is generally rolled up on the outerperipheral surface of a tubular core material (not shown) via therelease agent layer so that the adhesive layers are not brought intocontact with each other.

Next, the second biodegradable adhesive tape according to the inventionis described with reference to FIGS. 5 to 16 of the attached drawings.FIGS. 5 to 16 are each an enlarged sectional view showing one preferredembodiment of the second biodegradable adhesive tape of the invention.

The biodegradable adhesive tape 10 is composed of a biodegradabledouble-sided adhesive tape main body 20 and a double-sided release tape30.

In the biodegradable double-sided adhesive tape main body 20, anadhesive layer 2 is provided on each surface of the adhesive tapesubstrate 1 which is made up of only a biodegradable polymer layer (a).

The material of the biodegradable polymer layer (a), the thickness ofthe layer and the method for forming the layer are the same as those inthe embodiment shown in FIG. 1.

On both surfaces of the adhesive tape substrate 1, the adhesive layer 2is provided. The material of the adhesive layer 2 and the amount of theadhesive applied to the adhesive tape substrate 1 are the same as thosein the embodiment shown in FIG. 1.

The adhesive layer 2 can be obtained by, for example, coating the upperand the lower surfaces of the adhesive tape substrate 1 in order with asolution of the above-mentioned adhesive in a solvent such as toluene,xylene or ethyl acetate, and then drying the solution at a temperatureof 50° to 120° C.

The double-sided release tape 30 comprises a release tape substrate 4and a release agent layer 3, and the release agent layer 3 is formed oneach surface of the release tape substrate 4.

The release tape substrate 4 is formed from only the biodegradablepolymer layer (a), similarly to the adhesive tape substrate 1.

The thickness of the release tape substrate 4 composed of only thebiodegradable polymer layer (a) is the same as that of the adhesive tapesubstrate in the embodiment shown in FIG. 1.

The release tape substrate 4 composed of only the biodegradable polymerlayer (a) does not disrupt the natural environment even if thedouble-sided release tape 30 is discarded in the soil.

The material of the release agent layer 3 and the thickness thereof arethe same as those of the release agent layer formed on the adhesive tapesubstrate in the embodiment shown in FIG. 1.

Of the release agents of the natural compounds and the synthetic releaseagents as described above, those exhibiting biodegradability arepreferably used, because the natural environment is not disrupted evenif the double-sided release tape 30 is discarded in the soil.

The release agent layer 3 can be formed by coating the upper and lowersurfaces of the release tape substrate 4 in order with theabove-mentioned release agent by means of, for example, a roll coater.

In the biodegradable double-sided adhesive tape 10 consisting of thebiodegradable double-sided adhesive tape main body 20 and thebiodegradable double-sided release tape 30 as mentioned above, thebiodegradable double-sided adhesive tape main body 20 and thedouble-sided release tape 30 are superposed one upon another in such amanner that the adhesive layer 2 provided on one surface of the formerand the release agent layer 3 provided on one surface of the latter arebrought into contact with each other.

Further, the biodegradable double-sided adhesive tape 10 is stored or onthe market in the form of a roll which is made by winding thedouble-sided release tape 30 and the biodegradable double-sided adhesivetape maim body 20 which are combined together around a core with thedouble-sided release tape 30 being outside.

The biodegradable double-sided adhesive tape 10 shown in FIG. 6 is thesame as the biodegradable adhesive tape 10 shown in FIG. 5 except forthe adhesive tape substrate 1 of the biodegradable double-sided adhesivetape main body 20.

In the biodegradable double-sided adhesive tape main body 20 shown inFIG. 6, the adhesive tape substrate 1 is composed of a laminate of abiodegradable polymer layer (a) and a paper layer (b).

The material of the biodegradable polymer layer (a), the thickness ofthe layer, the method for forming the layer, the thickness of the paperlayer (b) and the method for laminating the biodegradable polymer layer(a) on the paper layer (b) are the same as those in the embodiment shownin FIG. 2.

The biodegradable double-sided adhesive tape 10 shown in FIG. 7 is alsothe same as the double-sided adhesive tape 10 shown in FIG. 5 except forthe adhesive tape substrate 1 of the biodegradable double-sided adhesivetape main body 20.

In the biodegradable double-sided adhesive tape main body 20 shown inFIG. 7, the adhesive tape substrate 1 is composed of a laminate havingthe laminated structure: biodegradable polymer layer (a)/paper layer(b)/biodegradable polymer layer (a).

The adhesive tape substrate 1 composed of such a laminate as mentionedabove can be obtained in the same manner as for the adhesive tapesubstrate 1 shown in FIG. 6 except that the biodegradable polymer layer(a), the paper layer (b) and the biodegradable polymer layer (a) aresuperposed one upon another in this order.

The biodegradable adhesive tape 10 shown in FIG. 8 is the same as thedouble-sided adhesive tape 10 shown in FIG. 5 except that the adhesivetape substrate 1 is composed of a laminate of a biodegradable polymerlayer (a) and a metallic thin film (c) and that the metallic thin film(c) is provided between the biodegradable polymer layer (a) and theadhesive layer 2.

In the biodegradable adhesive tape of this invention, a metallic oxidethin film layer may be formed in place of the metallic thin film layer(c).

The material of the biodegradable polymer layer a and the thicknessthereof are the same as those described above.

The material of the metallic thin film layer (c) (or the metallic oxidethin film layer), the thickness of the layer and the method for formingthe layer are the same as those in the embodiment shown in FIG. 4.

The biodegradable double-sided adhesive tape 10 shown in FIG. 9 is thesame as the biodegradable adhesive tape 10 shown in FIG. 5 except forthe release tape substrate 4 of the double-sided release tape 30.

In the biodegradable double-sided release tape 30 shown in FIG. 9, therelease tape substrate 3 is made up of only a paper layer (b).

The biodegradable double-sided adhesive tape 10 shown in FIG. 10 is alsothe same as the biodegradable double-sided adhesive tape 10 shown inFIG. 5 except for the release tape substrate 4 of the double-sidedrelease tape 30.

In the double-sided release tape 30 shown in FIG. 10, the release tapesubstrate 4 is composed of a laminate having the laminated structure:biodegradable polymer layer (a)/paper layer (b)/biodegradable polymerlayer (a).

In the present invention, the following embodiments are also availableother than the above-described ones.

i) a biodegradable double-sided adhesive tape 10, as illustrated in FIG.11, which is constituted by bonding the adhesive layer 2 provided on onesurface of the biodegradable double-sided adhesive tape main body 20shown in FIG. 6 to the release agent layer 3 provided on one surface ofthe double-sided release tape 30 shown in FIG. 9;

ii) a biodegradable doubIe-sided adhesive tape 10, as illustrated inFIG. 12, which is constituted by bonding the adhesive layer 2 providedon one surface of the biodegradable double-sided adhesive tape main body20 shown in FIG. 6 to the release agent layer 3 provided on one surfaceof the double-sided release tape 30 shown in FIG. 10;

iii) a biodegradable double-sided adhesive tape 10, as illustrated inFIG. 13, which is constituted by bonding the adhesive layer 2 providedon one surface of the biodegradable double-sided adhesive tape main body20 shown in FIG. 7 to the release agent layer 3 provided on one surfaceof the double-sided release tape 30 shown in FIG. 9;

iv) a biodegradable double-sided adhesive tape 10, as illustrated inFIG. 14, which is constituted by bonding the adhesive layer 2 providedon one surface of the biodegradable double-sided adhesive tape main body20 shown in FIG. 7 to the release agent layer 3 provided on one surfaceof the double-sided release tape 30 shown in FIG. 10;

v) a biodegradable double-sided adhesive tape 10, as illustrated in FIG.15, which is constituted by bonding the adhesive layer 2 provided on onesurface of the biodegradable double-sided adhesive tape main body 20shown in FIG. 8 to the release agent layer 3 provided on one surface ofthe double-sided release tape 30 shown in FIG. 9; and

vi) a biodegradable double-sided adhesive tape 10, as illustrated inFIG. 16, which is constituted by bonding the adhesive layer 2 providedon one surface of the biodegradable double-sided adhesive tape main body20 shown in FIG. 8 to the release agent layer 3 provided on one surfaceof the double-sided release tape 30 shown in FIG. 10.

Next, the biodegradable adhesive label according to the invention willbe described with reference to FIGS. 17 to 29 of the attached drawings.FIGS. 17 to 20 are each an enlarged sectional view showing one preferredembodiment of the biodegradable adhesive label of the invention.

The biodegradable adhesive label 10 shown in FIG. 17 is formed from abiodegradable adhesive label main body 20 and a release sheet 30.

In the biodegradable adhesive label main body 20, an adhesive layer 2 islaminated on one surface of an adhesive label substrate 1 composed ofonly a biodegradable polymer layer (a).

The material of the biodegradable polymer layer (a), the thickness ofthe layer and the method for forming the layer are the same as those forthe adhesive tape substrate in the embodiment shown in FIG. 1.

On one surface of the adhesive label substrate 1, the adhesive layer 2is formed. The material of this adhesive layer 2, the amount of theadhesive applied onto the substrate and the method for forming the layerare the same as those for the adhesive layer in the embodiment shown inFIG. 1.

The release sheet 30 consists of a release sheet substrate 4 and arelease agent layer 3, and the release agent layer 3 is formed on onesurface of the release sheet substrate 4.

In this embodiment, the release sheet substrate 4 is made up of only apaper layer.

With respect to the release agent layer 3 provided on such paper releasesheet substrate 4, the material of the layer, the thickness thereof andthe method for forming the layer are the same as those for the releaseagent layer in the embodiment shown in FIG. 5.

The biodegradable adhesive label of this embodiment is constituted bybonding the adhesive layer 2 of the biodegradable adhesive label mainbody 20 to the release agent layer 3 of the release sheet 30 describedabove.

The adhesive label 10 shown in FIG. 18 is the same as the biodegradableadhesive label 10 shown in FIG. 17 except for the adhesive labelsubstrate 1 of the biodegradable adhesive label main body 20.

In the biodegradable adhesive label main body 20 shown in FIG. 18, theadhesive label substrate 1 is composed of a laminate of a biodegradablepolymer layer (a) and a paper layer (b).

The material of the biodegradable polymer layer (a), the thickness ofthe layer, the method for forming the layer, the thickness of the paperlayer (b) and the method for laminating the biodegradable polymer layer(a) on the paper layer (b) are the same as those for the adhesive tapesubstrate in the embodiment shown in FIG. 2.

The biodegradable adhesive label 10 shown in FIG. 19 is also the same asthe biodegradable adhesive label 10 shown in FIG. 17 except for theadhesive label substrate 1 of the biodegradable adhesive label main body20.

In the biodegradable adhesive label main body 20 shown in FIG. 19, theadhesive label substrate 1 is composed of a laminate of a biodegradablepolymer layer (a) and a metallic thin film (c). In place of the metallicthin film (c), a metallic oxide thin film such as a silica thin film maybe provided.

The material of the biodegradable polymer layer (a) and the thicknessthereof are the same as those described above.

Further, the material of the metallic thin film layer (c) (or themetallic oxide thin film layer), the thickness of the layer and themethod for forming the layer are the same as those for the adhesive tapesubstrate in the embodiment shown in FIG. 4.

The adhesive label 10 shown in FIG. 20 is the same as the biodegradableadhesive label 10 shown in FIG. 17 except that the release sheetsubstrate 4 of the release sheet 30 is composed of a non-biodegradablepolymer layer (d).

The non-biodegradable polymer layer (d) is formed from a conventionallyknown non-biodegradable polymer such as polyvinyl chloride,polyvinylidene fluoride or polyethylene, and the thickness of the layer(d) is the same as that of the above-mentioned biodegradable polymerlayer (a).

The adhesive label of the invention is described above with respect tosome embodiments in which the release sheet is composed of only thepaper layer, only the non-biodegradable polymer layer or the laminate ofthe paper layer and the non-biodegradable polymer layer. However, theadhesive label of the invention may include other embodiments than thoseshown in FIGS. 17 to 20, so far as they do not deviate the scope of thepatent claims of the invention. For example, in the adhesive label ofthe invention, the release sheet substrate of the release sheet may beformed from a laminate of a paper layer and a non-biodegradable polymerlayer, or it may be formed from a laminate of a non-biodegradablepolymer layer, a paper layer and a non-biodegradable polymer layer.

Further, in the adhesive label of the invention, the release sheetsubstrate may be composed of a biodegradable polymer layer, or it may becomposed of a laminate of a paper layer and a biodegradable polymerlayer. Some embodiments having these constitutions are described below.

FIGS. 21 to 29 are each an enlarged sectional view of a preferredembodiment of the biodegradable adhesive label according to theinvention.

The biodegradable adhesive label 10 shown in FIG. 21 is formed from abiodegradable adhesive label main body 20 and a biodegradable releasesheet 30.

The biodegradable adhesive label main body 20 is the same as thebiodegradable label main body 20 shown in FIG. 17.

In the biodegradable release sheet 30, a release agent layer 3 islaminated on a release sheet substrate 4 which is composed of only abiodegradable polymer layer (a).

The material of the release sheet substrate 4 composed of only thebiodegradable polymer layer (a), the thickness of the substrate and themethod for forming the substrate are the same as those for the adhesivetape substrate in the embodiment shown in FIG. 1.

The release sheet substrate 4 composed of only the biodegradable polymerlayer (a) does not disrupt the natural environment even if thebiodegradable release sheet 30 is discarded in the soil, and thereforesuch release sheet substrate is preferably used for the invention.

The material of the release agent layer 3, the thickness of the layerand the method for forming the layer are the same as those for therelease agent layer of the biodegradable adhesive label shown in FIG.17.

In this embodiment, the release agent layer 3 formed from a releaseagent exhibiting biodegradability is particularly preferably used,because the natural environment is not disrupted even if thebiodegradable release sheet 30 is discarded in the soil.

The biodegradable adhesive label 10 shown in FIG. 22 is the same as theembodiment shown in FIG. 21 except that the biodegradable adhesive labelmain body 20 is the same as that in the biodegradable adhesive labelshown in FIG. 18.

The biodegradable adhesive label 10 shown in FIG. 23 is the same as theembodiment shown in FIG. 21 except that the biodegradable adhesive labelmain body 20 is the same as that in the biodegradable adhesive labelshown in FIG. 19.

The biodegradable adhesive label 10 shown in FIG. 24 is the same as thebiodegradable adhesive label shown 10 in FIG. 21 except for the releasesheet substrate 4 of the biodegradable release sheet 30.

In the biodegradable release sheet 30 shown in FIG. 24, the releasesheet substrate 4 is composed of a laminate of a biodegradable polymerlayer (a) and a paper layer (b), and the release agent layer 3 is formedon the biodegradable polymer layer (a).

The material of the biodegradable polymer layer (a), the thickness ofthe layer and the method for forming the layer, the thickness of thepaper layer (b) and the method for laminating the biodegradable polymerlayer (a) on the paper layer (b) are the same as those for thebiodegradable adhesive label main body 20 in the embodiment shown inFIG. 18.

The biodegradable adhesive label 10 shown in FIG. 25 is also the same asthe biodegradable adhesive label 10 shown in FIG. 21 except for therelease sheet substrate 4 of the biodegradable release sheet 30.

In the biodegradable release sheet 30 shown in FIG. 25, the releasesheet substrate 4 is composed of a laminate having the laminatedstructure: biodegradable polymer layer (a)/paper layer (b)/biodegradablepolymer layer (a).

The release sheet substrate 4 having such a three-layer structure asmentioned above can be obtained in the same manner as for the releasesheet substrate 4 in the embodiment shown in FIG. 10, that is, it can beobtained by superposing the biodegradable polymer layer (a), the paperlayer (b) and the biodegradable polymer layer (a) one upon another inthis order.

In the present invention the following embodiments are also availableother than the above-described ones.

i) a biodegradable adhesive label 10 illustrated in FIG. 26, which isconstituted by bonding the adhesive layer 2 provided on one surface ofthe biodegradable adhesive label main body 20 shown in FIG. 22 to therelease agent layer 3 provided on one surface of the biodegradablerelease sheet 30 shown in FIG. 24;

ii) a biodegradable adhesive label 10 illustrated in FIG. 27, which isconstituted by bonding the adhesive layer 2 provided on one surface ofthe biodegradable adhesive label main body 20 shown in FIG. 22 to therelease agent layer 3 provided on one surface of the biodegradablerelease sheet 30 shown in FIG. 25;

iii) a biodegradable adhesive label 10 illustrated in FIG. 28, which isconstituted by bonding the adhesive layer 2 provided on one surface ofthe biodegradable adhesive label main body 20 shown in FIG. 23 to therelease agent layer 3 provided on one surface of the biodegradablerelease sheet 30 shown in FIG. 24; and

iv) a biodegradable adhesive label 10 illustrated in FIG. 29, which isconstituted by bonding the adhesive layer 2 provided on one surface ofthe biodegradable adhesive label main body 20 shown in FIG. 23 to therelease agent layer 3 provided on one surface of the biodegradablerelease sheet 30 shown in FIG. 25.

EFFECT OF THE INVENTION

According to the present invention, as described above, the naturalenvironment is not disrupted or the ecosystem is not largelydisorganized even if the adhesive tape and the adhesive label arediscarded in the soil, because they use a biodegradable polymer as amaterial of their substrates.

EXAMPLE

The present invention is further described with reference to thefollowing examples, but it should be construed that the invention is inno way limited to those examples.

Example 1

One surface of a film made of a polymer alloy of starch and denaturedpolyvinyl alcohol (trade name: Matabee ZF03U, Novamont Co., U.S.A.) andhaving a thickness of 40 μm, which was a biodegradable polymer layer,was coated with shellac as a release agent to form a release agent layerhaving a thickness of 0.05 μm.

Then, the other surface of the biodegradable polymer layer was coatedwith a toluene solution containing a mixture of natural rubber and aterpene resin as an adhesive and having a concentration of 20% in anamount of 30 g/m² by means of a comma coater to form an adhesive layer.Thus, a biodegradable adhesive tape having a structure shown in FIG. 1was obtained.

The biodegradable adhesive tape thus obtained was cut to have a width of25 mm, and two of the resulting biodegradable adhesive tapes were bondedtogether in such a manner the adhesive layer of one tape was contactedwith the release agent layer of the other tape. Then, thosebiodegradable adhesive tapes are peeled from each other under theconditions of a temperature of 23° C., a humidity of 65% RH, a peel rateof 300 mm/min and a peel angle of 180° to measure the peel strength.

Further, the biodegradable adhesive tape having a width of 25 mm wasbonded to a surface of SUS304 (JIS: stainless steel) in such a mannerthat the adhesive layer of the adhesive tape was contacted with thesurface of SUS304. Then, the biodegradable adhesive tape was peeled fromthe SUS304 under the same conditions as described above to measure thepeel strength. From the peel strength, the adhesion strength of thebiodegradable adhesive tape was evaluated.

The biodegradable adhesive tape obtained in the above was cut to give asample having a size of 100 mm×100 mm. The sample was buried in the soilat the depth of 10 cm, allowed to stand for 1 month and 3 months, anddug up. The degree of degradation of the biodegradable adhesive tape wascalculated by the following formula 1: ##EQU1##

The results are set forth in Table 1.

Comparative Example 1

An adhesive tape for comparison was prepared in the same manner asdescribed in Example 1 except that a polypropylene film (trade name:Alphan SY101, available from Honshu Paper Mfg. Co., Ltd.) having thesame thickness (40 μm) as that of the biodegradable polymer layer wasused in place of the biodegradable polymer layer. The adhesive tape thusobtained was evaluated on the peel strength, the adhesion strength andthe degree of degradation.

The results are set forth in Table 1.

                  TABLE 1    ______________________________________                       Degree of Degradation                       (%)           Peel    Adhesion  1 month   3 months           Strength                   Strength  in the    in the           (g/25 mm)                   (g/25 mm) soil      soil    ______________________________________    Example 1             160       1,500     30      50    Comp. Ex. 1             200       1,400     5       10    ______________________________________

Example 2

On both surfaces of a woodfree paper (available from LINTEC CORPORATION)having a basis weight of 80 g/m² was laminated a biodegradable polymermade of a polymer alloy of starch and denatured polyvinyl alcohol (tradename: Matabee ZF03U, Novamont Co., U.S.A.) at a heating temperature of150° C. by means of an extrusion molding machine to form biodegradablepolymer layers each having a thickness of 12 μm, whereby a release tapesubstrate consisting of a biodegradable polymer layer, a paper layer anda biodegradable polymer layer was obtained.

On each of the biodegradable polymer layers on both sides of the releasetape substrate, a silicone release agent layer was formed using asilicon release agent (trade name: SRX244, available from Toray SiliconeK.K.), to obtain a double-sided release tape.

Then, one surface of the above-mentioned biodegradable polymer filmhaving a thickness of 40 μm, which was an adhesive tape substrate, wascoated with a toluene solution containing a mixture of natural rubberand a terpene resin as an adhesive and having a concentration of 20% inan amount of 30 g/m² by means of a comma coater to form an adhesivelayer.

The adhesive layer and the double-sided release tape were bondedtogether. Then, on the free surface of the adhesive tape substrate wasformed the same adhesive layer as mentioned above to prepare abiodegradable double-sided adhesive tape having such a structureconsisting of a biodegradable double-sided tape main body and a doublesided release tape as shown in FIG. 10.

The biodegradable double-sided adhesive tape thus obtained was cut tohave a width of 25 mm. Then, a polyester tape having a width of 25 mmwas superposed on the adhesive layer of the biodegradable double-sidedadhesive tape, and they are bonded to each other. Thereafter, thedouble-sided release tape was peeled from the biodegradable double-sidedadhesive tape. The adhesive layer of the resulting laminate consistingof the double-sided adhesive tape main body and the polyester tape wasbonded to the surface of SUS304, and the biodegradable adhesive tape wasthen peeled under the conditions of a temperature of 23° C., a humidityof 65% RH, a peel rate of 300 mm/min and a peel angle of 180° to measurethe adhesion strength of the double-sided adhesive tape main body.

The biodegradable double-sided adhesive tape was cut to give a samplehaving a size of 100 mm×100 mm. The sample was buried in the soil at thedepth of 10 cm, allowed to stand for 1 month and 3 months, and dug up.The degree of degradation of the biodegradable double-sided adhesivetape was calculated by the formula 1 of Example 1.

The results are set forth in Table 2.

Comparative Example 2

A double-sided adhesive tape for comparison was prepared in the samemanner as described in Example 2 except that a release tape substrateobtained by laminating polyethylene (trade name: Showflex L170,available from Showa Denko K.K.) with the same thickness as that of thebiodegradable polymer layer in place of the biodegradable polymer on thewoodfree paper at a heating temperature of 300° C. was used and that apolypropylene film (trade name: Alphan SY101, available from HonshuPaper Mfg. Co., Ltd.) with the same thickness as that of the adhesivetape substrate was used as the adhesive tape substrate. The double-sidedadhesive tape thus obtained was evaluated on the adhesion strength andthe degree of degradation.

The results are set forth in Table 2.

                  TABLE 2    ______________________________________                     Degree of Degradation                     (%)            Adhesion   1 month  3 months            Strength   in the   in the            (g/25 mm)  soil     soil    ______________________________________    Example 2 1,900        30       50    Comp. Ex. 2              1,800        10       25    ______________________________________

Example 3

On one surface of a film made from a copolymer of 3-hydroxybutyric acidand 3-hydroxysuccinic acid (trade name: Biopole, ICI Co., England) andhaving a thickness of 70 μm, which was a biodegradable polymer layer,aluminum was deposited at degree of vacuum of 5×10⁻⁵ torr to form analuminum thin film.

The aluminum thin film thus obtained was coated with a toluene solutioncontaining a mixture of natural rubber and a terpene resin as anadhesive and having a concentration of 20% in an amount of 30 g/m² bymeans of a comma coater to form an adhesive layer, whereby abiodegradable adhesive label main body was obtained.

Then, on both surfaces of a woodfree paper (available from LINTECCORPORATION) having a basis weight of 80 g/m², a polyethylene film(trade name: Showflex L170, Showa Denko K.K.) having a thickness of 12μm was laminated at a heating temperature of 300° C. by means of anextrusion molding machine to obtain a release sheet substrate comprisinga non-biodegradable polymer layer and a paper layer.

On the non-biodegradable polymer layer of the release sheet substrate, arelease agent layer was formed using a silicone release agent (tradename: SRX244, available from Toray Silicone K.K.), to obtain a releasesheet.

The adhesive layer of the biodegradable adhesive label main body wassuperposed on the release agent layer of the release sheet, and theywere bonded together to obtain a biodegradable adhesive label.

The biodegradable adhesive label thus obtained was cut to have a widthof 25 mm. Then, the biodegradable adhesive label main body was peeledfrom the release sheet, and the adhesive layer of the biodegradableadhesive label main body was bonded to the surface of SUS304.Thereafter, the adhesive label was peeled from the SUS304 under theconditions of a temperature of 23° C., a humidity of 65% RH, a peel rateof 300 mm/min and a peel angle of 180° to measure the peel strength.From the peel strength, the adhesion strength of the biodegradableadhesive label was evaluated.

The biodegradable adhesive label obtained in the above was cut to give asample having a size of 100 mm×100 mm. The sample was buried in the soilat the depth of 10 cm, allowed to stand for 1 month and 3 months, anddug up. The degree of degradation of the biodegradable adhesive labelwas calculated by the formula 1 of Example 1.

The results are set forth in Table 3.

Comparative Example 3

An adhesive label was prepared in the same manner as described inExample 3 except that a polyester film (trade name: Lumiler S-10,available from Toray industries, Inc.) having a thickness of 75 μm wasused as the adhesive label substrate. The adhesive label thus obtainedwas evaluated on the adhesion strength and the degree of degradation.

The results are set forth in table 3.

                  TABLE 3    ______________________________________                     Degree of Degradation                     (%)            Adhesion   1 month  3 months            Strength   in the   in the            (g/25 mm)  soil     soil    ______________________________________    Example 3 1,900        40       60    Comp. Ex. 3              1,800        20       25    ______________________________________

Example 4

On one surface of a film made from a copolymer of 3-hydroxybutyric acidand 3-hydroxysuccinic acid (trade name: Biopole, ICI Co., England) andhaving a thickness of 70 μm, which was a biodegradable polymer layer,aluminum was deposited at degree of vacuum of 5×10⁻⁵ torr to form analuminum thin film.

The aluminum thin film was coated with a toluene solution containing amixture of natural rubber and a terpene resin as an adhesive and havinga concentration of 20% in an amount of 30 g/m² by means of a commacoater to form an adhesive layer, whereby a biodegradable adhesive labelmain body was obtained.

Then, the biodegradable polymer layer was laminated on a woodfree paper(available from LINTEC CORPORATION) having a basis weight of 80 g/m² ata heating temperature of 200° C. by means of an extrusion moldingmachine to obtain a release sheet substrate comprising a biodegradablepolymer layer and a paper layer.

On the biodegradable polymer layer of the release sheet substrate, arelease agent layer was formed using a silicone release agent (tradename: SRX244, available from Toray Silicone K.K.), to obtain abiodegradable release sheet.

The adhesive layer of the biodegradable adhesive label main body wassuperposed on the release agent layer of the biodegradable releasesheet, and they were bonded together to obtain a biodegradable adhesivelabel.

The biodegradable adhesive label thus obtained was cut to have a widthof 25 mm. Then, the biodegradable adhesive label main body was peeledfrom the biodegradable release sheet, and the adhesive layer of thebiodegradable adhesive label main body was bonded to the surface ofSUS304. Thereafter, the adhesive label was peeled from the SUS304 underthe conditions of a temperature of 23° C., a humidity of 65% RH, a peelrate of 300 mm/min and a peel angle of 180° to measure the peelstrength. From the peel strength, the adhesion strength of thebiodegradable adhesive label was evaluated.

The biodegradable adhesive label was cut to give a sample having a sizeof 100 mm×100 mm. The sample was buried in the soil at the depth of 10cm, allowed to stand for 1 month and 3 months, and dug up. The degree ofdegradation of the biodegradable adhesive label was calculated by theformula 1 of Example 1.

The results are set forth in Table 4.

Comparative Example 4

An adhesive label was prepared in the same manner as described inExample 4 except that a polyester film (trade name: Lumiler S-10,available from Toray Industries, Inc.) having a thickness of 75 μm wasused as the adhesive label substrate and that a release sheet substrateobtained by laminating polyethylene (trade Name: Showflex L170,available from Showa Denko K.K.) on both surfaces of a woodfree paper(available from Rintec K.K.) having a basis weight of 80 g/m² at aheating temperature of 300° C. by means of an extrusion molding machinewas used. The adhesive label thus obtained was evaluated on the adhesionstrength and the degree of degradation.

The results are set forth in table 4.

                  TABLE 4    ______________________________________                     Degree of Degradation                     (%)            Adhesion   1 month  3 months            Strength   in the   in the            (g/25 mm)  soil     soil    ______________________________________    Example 4 1,900        40       60    Comp. Ex. 4              1,800        20       25    ______________________________________

What is claimed is:
 1. A biodegradable adhesive tape comprising:anadhesive tape substrate which comprises a biodegradable polymer layer; arelease agent layer formed on one surface of said substrate; and anadhesive layer formed on the other surface of said substrate, whereinsaid adhesive layer comprises a mixture of a natural rubber and at leastone tackifier resin selected from the group consisting of rosin,derivatives of rosin, terpene and derivatives of terpene and theadhesive tape substrate is a laminate comprising the biodegradablepolymer layer, and one of a metallic film layer and a metallic oxidefilm layer, said one of the metallic film layer and the metallic oxidefilm layer being positioned between the biodegradable polymer layer andthe adhesive layer.
 2. The adhesive tape as claimed in claim 1, whereinsaid derivative of rosin is selected from the group consisting ofhydrogenated rosin, disproportionated rosin, polymerized rosin and rosinester and said derivative of terpene is selected from the groupconsisting of α-pinene resin, β-pinene resin, dipentene resin andhydrogenated products thereof.
 3. A biodegradable adhesive tapecomprising:a biodegradable double-sided adhesive tape main bodycomprising an adhesive tape substrate which comprises a biodegradablepolymer layer and adhesive layers formed on both surfaces of theadhesive tape substrate, said adhesive layers each comprising a mixtureof a natural rubber and at least one tackifier resin selected from thegroup consisting of rosin, derivatives of rosin, terpene and derivativesof terpene; and a double-sided release tape comprising a release tapesubstrate and release agent layers formed on both surfaces of therelease tape substrate, wherein the biodegradable double-sided adhesivetape main body and the double-sided release tape are laminated togetherin such a manner that the adhesive layer of the biodegradabledouble-sided adhesive tape main body is in contact with the releaseagent layer of the double-sided release tape.
 4. The biodegradableadhesive tape as claimed in claim 3, wherein the adhesive tape substrateconsists of the biodegradable polymer layer.
 5. The biodegradableadhesive tape as claimed in claim 3, wherein the adhesive tape substrateis a laminate comprising the biodegradable polymer layer and a paperlayer.
 6. The biodegradable adhesive tape as claimed in claim 3, whereinthe adhesive tape substrate is a laminate having a laminated structureof the biodegradable polymer layer/a paper layer/the biodegradablepolymer layer.
 7. The biodegradable adhesive tape as claimed in claim 6,wherein the adhesive tape substrate is a laminate comprising thebiodegradable polymer layer, and one of a metallic film layer and ametallic oxide film layer.
 8. The biodegradable adhesive tape as claimedin claim 3, wherein the release tape substrate consists of abiodegradable polymer layer.
 9. The biodegradable adhesive tape asclaimed in claim 3, wherein the release tape substrate is a paper layer.10. The biodegradable adhesive tape as claimed in claim 3, wherein therelease tape substrate is a laminate having a laminated structure of abiodegradable polymer layer/a paper layer/a biodegradable polymer layer.11. The double-sided adhesive tape as claimed in claim 3, wherein saidderivative of rosin is selected from the group consisting ofhydrogenated rosin, disproportionated rosin, polymerized rosin and rosinester and said derivative of terpene is selected from the groupconsisting of α-pinene resin, β-pinene resin, dipentene resin andhydrogenation products thereof.
 12. A biodegradable adhesive labelcomprising:an adhesive label main body comprising an adhesive labelsubstrate and an adhesive layer formed on the adhesive label substrate,wherein said adhesive label substrate comprises a biodegradable polymerand said adhesive layer comprises a mixture of a natural rubber and atleast one tackifier resin selected from the group consisting of rosin,derivatives of rosin, terpene and derivatives of terpene; and a releasesheet comprising a release sheet substrate having a layer formed from amaterial selected from a paper, a non-biodegradable polymer and abiodegradable polymer and a release agent layer formed on the releasesheet substrate, wherein the biodegradable adhesive label main body andthe release sheet are laminated together in such a manner that theadhesive layer of the biodegradable adhesive label main body is incontact with the release agent layer of the release sheet.
 13. Thebiodegradable adhesive label as claimed in claim 12, wherein theadhesive label substrate consists of the biodegradable polymer layer.14. The biodegradable adhesive label as claimed in claim 12, wherein theadhesive label substrate is a laminate of the biodegradable polymerlayer and a paper layer, and the adhesive layer is formed on said paperlayer.
 15. The biodegradable adhesive label as claimed in claim 12,wherein the adhesive label substrate is a laminate consisting of thebiodegradable polymer layer, and one of a metallic film and a metallicoxide film, and the adhesive layer is formed on said one of the metallicfilm and the metallic oxide film.
 16. The biodegradable adhesive labelas claimed in claim 12, wherein the release sheet substrate consists ofa paper layer.
 17. The biodegradable adhesive label as claimed in claim12, wherein the release sheet substrate consists of a non-biodegradablepolymer layer.
 18. The biodegradable adhesive label as claimed in claim12, wherein the release sheet substrate is a laminate of a paper layerand a non-biodegradable polymer layer, and the release agent layer isformed on said non-biodegradable polymer layer.
 19. The biodegradableadhesive label as claimed in claim 12, wherein the release sheetsubstrate is a laminate having a laminated structure of anon-biodegradable polymer layer/a paper layer/a non-biodegradablepolymer layer.
 20. The biodegradable adhesive label as claimed in claim12, wherein the release sheet substrate consists of a biodegradablepolymer layer.
 21. The biodegradable adhesive label as claimed in claim12, wherein the release sheet substrate is a laminate of a paper layerand a biodegradable polymer layer, and the release agent layer is formedon said biodegradable polymer layer.
 22. The biodegradable adhesivelabel as claimed in claim 12, wherein the release sheet substrate is alaminate having a laminated structure of a biodegradable polymer layer/apaper layer/a biodegradable polymer layer.
 23. The adhesive label asclaimed in claim 12, wherein said derivative of rosin is selected fromthe group consisting of hydrogenated rosin, disproportionated rosin,polymerized rosin and rosin ester and said derivative of terpene isselected from the group consisting of α-pinene resin, β-pinene resin,dipentene resin and hydrogenation products thereof.